Introduction & Characteristics:
FRW-91Ni2 is a rutile and micro-alloyed type flux cored wire designed for all position welding with CO2 shielding gas and 620Mpa grade high tensile strength steel,it contains 2.0%-3.0% Ni and has good impcat value at low temperature down to -40ºC.
Typical application: low temperature service steels such as ASTM A302,A572,A575,A734.
Instructions:
1.The oil stains and rust on the weldments should be cleared away.
2. Designed for welding with 100% CO2.
3. When welding, the gas flow rate is generally 20~25L/min.
FRW-91Ni2 is a rutile and micro-alloyed type flux cored wire designed for all position welding with CO2 shielding gas and 620Mpa grade high tensile strength steel,it contains 2.0%-3.0% Ni and has good impcat value at low temperature down to -40ºC.
Typical application: low temperature service steels such as ASTM A302,A572,A575,A734.
Instructions:
1.The oil stains and rust on the weldments should be cleared away.
2. Designed for welding with 100% CO2.
3. When welding, the gas flow rate is generally 20~25L/min.
Chemical compostiton of deposited metal (shield gas:CO2)
C | Mn | Si | P | S | Ni | Mo |
0.05 | 1.1 | 0.4 | 0.015 | 0.012 | 2.37 | 0.19 |
Mechanical properties of deposited metal (shield gas:CO2)
Yield Strength | Tensile Strength | Elongation | Impact Value |
Mpa(σb) | Mpa(σb) | %(δ5) | -40ºC(J) |
620 | 680 | 24 | 76 |
Sizes available and recommended currents(DC-EP)
Diameter(mm) | 1.2 | 1.4 | 1.6 | |
Current(A) | F | 120-300 | 150-380 | 180-430 |
HF | 120-260 | 150-320 | 180-380 | |
V,OH | 120-260 | 150-270 | 180-280 | |
H | 120-280 | 150-320 | 180-330 | |
VD | 200-280 | 220-300 | 250-300 |
Package
Dia(mm) | 1.2 | 1.4 | 1.6 |
Spool(kg)/(lbs) | 5,12.5,15,20/11,28,33 | ||
Pailpack(kg) | 100-300 |